PLA SILK filament (1.75 mm) is made in Europe for 3D printers using FFF/FDM technology.

PLA SILK has been enhanced with added polymers that give the material its high level of light dispersion and reflection, achieving the silky surface finish that defines this filament. With PLA as its main material, it keeps the properties and advantages of standard PLA (easy modelling, no warping and low shrinkage) and even surpasses it in some respects, as it has greater mechanical and thermal resistance than PLA.

Features:

-Diameter 1.75 mm.

-1000 gram spool.

General printing parameters:

-Nozzle temperature (between 200ºC and 230ºC)

-Bed temperature (between 50ºC and 70ºC)

-Ventilador: LIGADO (100) %

Propriedades físicas:

-Densidade: 1,24 g/cm3

- Caudal: 8 g/10 min (ISO 1133-A)

- Caudal: 3 g/10 min (ISO 1133-A)

-Stereochemical purity: 96 (% L-isomer)

- Monómero residual: 0,3% (máx.)

-Humidade (Karl Fisher Coulométrico): 400 (máx.) ppm

-Melting temperature: 155º C Tm (DSC)

-Glass transition temperature: 55-60º C Tg (DSC)

Propriedades mecânicas:

-Tensile modulus: 3500 MPa (ISO 527-1)

- Resistência à tracção: 45 MPa (ISO 527-1)

- Yield strain: 5% (max.) (ISO 527-1)

- Impacto entalhado Charpy 23º C: ≤5 kJ/m2 (ISO 179-1eA)

Sample 3D-printed figure not included.